ID 117038
タイトル別表記
レジン添加型グラスアイオノマーセメントの電気伝導度と通電によるせん断試験強度低下に塩化ナトリウム溶液浸漬が与える影響
著者
松木, 佑太 徳島大学大学院口腔科学教育部(口腔科学専攻)
佐藤, 博子 Tokushima University
Kajimoto, Noboru Fukuoka Dental College
キーワード
Glass-ionomer-cement
Shear bonding strength
Electrical conductivity
Smart dental cement
Debonding-on-demand
Electrical shear bond strength reduction
資料タイプ
学位論文
抄録
Advancements in dental cements have considerably improved their bond strengths. However, high bond strength often makes the removal of restorations difficult. Thus, smart dental cements that show controllable bond strength are required. A conventional resin-modified glass-ionomer-cement demonstrated a significant reduction in the bond strength after current application. However, for this system, the ions in the cement are released into the oral cavity, resulting in a reduction of the electrical conductivity and in losses of the expected on-demand debonding property. Herein, the effects of immersion in 0.9 and 15% NaCl solutions on the electrical conductivity and debonding properties were investigated. The cement immersed in 0.9% NaCl solution from 1 to 28 days maintained similar bond strength reductions after current application, whereas that in 15% NaCl solution initially showed no bond strength reduction after 1 day but exhibited an increase in the bond strength reduction after immersion for 28 days.
掲載誌名
Dental Materials Journal
ISSN
02874547
18811361
cat書誌ID
AA10443149
出版者
The Japanese Society for Dental Materials and Devices
41
3
開始ページ
487
終了ページ
494
発行日
2022-05-25
備考
内容要旨・審査要旨・論文本文の公開
本論文は,著者Yuta MATSUKIの学位論文として提出され,学位審査・授与の対象となっている。
権利情報
© 2022 The Japanese Society for Dental Materials and Devices
EDB ID
出版社版DOI
出版社版URL
フルテキストファイル
言語
eng
著者版フラグ
博士論文全文を含む
文科省報告番号
甲第3614号
学位記番号
甲口第484号
学位授与年月日
2022-03-23
学位名
博士(歯学)
学位授与機関
徳島大学
部局
歯学系
病院