タイトル別表記 | ボールミリング法で改質したβ-TCPセメントの諸特性への粉液比の影響
|
著者 |
裵, 志英
Tokushima University
|
キーワード | Injectability
β-TCP
Mechanical properties
Compressive strength in vivo
|
資料タイプ |
学位論文
|
抄録 | The authors have developed a β-tricalcium-phosphate (β-TCP) powder modified mechano-chemically through the application of a ball-milling process (mβ-TCP). The resulting powder can be used in a calcium-phosphate-cement (CPC). In this study, the effects of the powder-to-liquid ratio (P/L ratio) on the properties of the CPCs were investigated, and an appropriate P/L ratio that would simultaneously improve injectability and strength was clarified. The mβ-TCP cement mixed at a P/L ratio of 2.5 and set in air exhibited sufficient injectability until 20 min after mixing, and strength similar to or higher than that mixed at a P/L ratio of 2.0 and 2.78. Although the mβ-TCP cements set in vivo and in SBF were found to exhibit a lower strength than those set in air, it did have an appropriate setting time and strength for clinical applications. In conclusion, P/L ratio optimization successfully improved the strength of injectable mβ-TCP cement.
|
掲載誌名 |
Dental Materials Journal
|
ISSN | 18811361
02874547
|
cat書誌ID | AA10443149
|
出版者 | The Japanese Society for Dental Materials and Devices
|
巻 | 36
|
号 | 5
|
開始ページ | 590
|
終了ページ | 599
|
発行日 | 2017-09-25
|
備考 | 内容要旨・審査要旨・論文本文の公開:
内容要旨:LID201705101001.pdf 審査要旨:LID201705101002.pdf 論文本文:LID201705251001.pdf 本論文は,著者Yumika IDAの学位論文として提出され,学位審査・授与の対象となっている。 |
権利情報 | © 2017 The Japanese Society for Dental Materials and Devices
|
EDB ID | |
出版社版DOI | |
出版社版URL | |
フルテキストファイル | |
言語 |
eng
|
著者版フラグ |
博士論文全文を含む
|
文科省報告番号 | 甲第3079号
|
学位記番号 | 甲口第422号
|
学位授与年月日 | 2017-03-23
|
学位名 |
博士(歯学)
|
学位授与機関 |
徳島大学
|
部局 |
歯学系
|