ID 111978
Title Alternative
ボールミリング法で改質したβ-TCPセメントの諸特性への粉液比の影響
Author
Ida, Yumika Tokushima University
Bae, Jiyoung Tokushima University
Keywords
Injectability
β-TCP
Mechanical properties
Compressive strength in vivo
Content Type
Thesis or Dissertation
Description
The authors have developed a β-tricalcium-phosphate (β-TCP) powder modified mechano-chemically through the application of a ball-milling process (mβ-TCP). The resulting powder can be used in a calcium-phosphate-cement (CPC). In this study, the effects of the powder-to-liquid ratio (P/L ratio) on the properties of the CPCs were investigated, and an appropriate P/L ratio that would simultaneously improve injectability and strength was clarified. The mβ-TCP cement mixed at a P/L ratio of 2.5 and set in air exhibited sufficient injectability until 20 min after mixing, and strength similar to or higher than that mixed at a P/L ratio of 2.0 and 2.78. Although the mβ-TCP cements set in vivo and in SBF were found to exhibit a lower strength than those set in air, it did have an appropriate setting time and strength for clinical applications. In conclusion, P/L ratio optimization successfully improved the strength of injectable mβ-TCP cement.
Journal Title
Dental Materials Journal
ISSN
18811361
02874547
NCID
AA10443149
Publisher
The Japanese Society for Dental Materials and Devices
Volume
36
Issue
5
Start Page
590
End Page
599
Published Date
2017-09-25
Remark
内容要旨・審査要旨・論文本文の公開:
内容要旨:LID201705101001.pdf
審査要旨:LID201705101002.pdf
論文本文:LID201705251001.pdf
本論文は,著者Yumika IDAの学位論文として提出され,学位審査・授与の対象となっている。
Rights
© 2017 The Japanese Society for Dental Materials and Devices
EDB ID
DOI (Published Version)
URL ( Publisher's Version )
FullText File
language
eng
TextVersion
ETD
MEXT report number
甲第3079号
Diploma Number
甲口第422号
Granted Date
2017-03-23
Degree Name
Doctor of Dental Science
Grantor
Tokushima University
departments
Oral Sciences