著者
Ueshima, Tomoe Tokushima University
Takatani, Masahiro Tokushima University
Sugiura, Hikaru Tokushima University
Ominami, Kota Tokushima University
資料タイプ
学術雑誌論文
抄録
Porous stainless steel (SUS) supports were modified with double intermediate layers, silicalite-1 and γ-alumina, to enhance the hydrogen diffusion of a thin palladium membrane. One of layers, silicalite-1, was prepared using the hydrothermal synthetic method on porous SUS supports. The differences in expansion/contraction behaviors caused by different thermal coefficients of expansion between silicalite-1 and the SUS resulted in a lowering of the durability of the membrane. Intermediates layers of mesoporous MCM-48 powders or commercial spherical non-porous silica particles were then applied to porous SUS supports via aspiration, γ-alumina was introduced by dip-coating, and the Pd membrane was subjected to electro-less plating. H2 permeance of the Pd membrane (membrane thickness: 11 μm) containing spherical silica particles was around 10 × 10−6 mol·m−2·s−1·Pa−1 at 600 °C, which was higher than that of the Pd membrane (membrane thickness: 7 μm) containing MCM-48. The durability of the Pd membrane containing spherical silica particles was higher than that of the version containing MCM-48 powders. These results suggest that commercial spherical non-porous silica particles will uniformly occupy the pores of the SUS tubes and enhance the H2 permeance and durability of the Pd membrane.
掲載誌名
Scientific Reports
ISSN
20452322
出版者
Springer Nature
10
開始ページ
5148
発行日
2020-03-20
権利情報
This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/.
EDB ID
出版社版DOI
出版社版URL
フルテキストファイル
言語
eng
著者版フラグ
出版社版
部局
理工学系