Fabrication of Chitin Nanofiber-Reinforced Polylactic Acid Nanocomposites by an Environmentally Friendly Process

Polylactic acid (PLA) reinforced with chitin nanofibers was produced from a mixture of a colloidal suspension of PLA particles with chitin nanofiber suspension. The dispersion medium was solely water, which was removed by filtration and drying. Nanocomposites were obtained by compression molding of the filtrates. Static tensile test and dynamic mechanical analysis were performed to evaluate the reinforcement as a function of nanofiber content. Chitin nanofibers delivered reinforcement similar to cellulose nanofibers, being especially effective at up to 70 wt% fiber load. The ultimate tensile modulus and strength reached 7.7 GPa and 110 MPa, respectively, at a nanofiber content of 70 wt%.