Synthesis of titanium nitride for self-aligned gate AlGaN/GaN heterostructure field-effect transistors

In this study, titanium nitride (TiN) is synthesized using reactive sputtering for a self-aligned gate process. The Schottky barrier height of the TiN on n-GaN is around 0.5 to 0.6 eV and remains virtually constant with varying nitrogen ratios. As compared with the conventional Ni electrode, the TiN electrode presents a lower turn-on voltage, while its reverse leakage current is comparable with that of Ni. The results of annealing evaluation at different temperatures and duration times show that the TiN/W/Au gate stack can withstand the ohmic annealing process at 800°C for 1 or 3 min. Finally, the self-aligned TiN-gated AlGaN/GaN heterostructure field-effect transistors are obtained with good pinch-off characteristics.

This is an Open Access article distributed under the terms of the Creative Commons Attribution License (http://creativecommons.org/licenses/by/4.0), which permits unrestricted use, distribution, and reproduction in any medium, provided the original work is properly credited.