ID | 109868 |
著者 |
エヒロ, タクヤ
Department of Chemical Science and Technology, Tokushima University
イタガキ, アイ
Department of Chemical Science and Technology, Tokushima University
倉科, 昌
Department of Life System, Institute of Technology and Science, Tokushima University
徳島大学 教育研究者総覧
KAKEN研究者をさがす
加藤, 雅裕
Department of Advanced Materials, Institute of Technology and Science, Tokushima University
徳島大学 教育研究者総覧
KAKEN研究者をさがす
中川, 敬三
Department of Advanced Materials, Institute of Technology and Science, Tokushima University|Department of Resource Circulation Engineering, Center for Frontier Research of Engineering, Tokushima University
KAKEN研究者をさがす
カトウ, ユウキ
Otake Research Laboratories, Mitsubishi Rayon Co. Ltd.
ニノミヤ, ワタル
Otake Research Laboratories, Mitsubishi Rayon Co. Ltd.
杉山, 茂
Department of Advanced Materials, Institute of Technology and Science, Tokushima University|Department of Resource Circulation Engineering, Center for Frontier Research of Engineering, Tokushima University
徳島大学 教育研究者総覧
KAKEN研究者をさがす
|
キーワード | Template ion exchange
FSM-16
Chromium
Oxidative dehydrogenation
Isobutane
|
資料タイプ |
学術雑誌論文
|
抄録 | The template ion exchange of chromium cations into FSM-16 (#16 Folded Sheets Mesoporous Materials) for 247 h resulted in a 2.89 wt% incorporation of those cations into the FSM-16, although only a 0.3 wt% incorporation had previously been reported. The XRD pattern of the resultant solid (Cr-FSM-16) showed that the hexagonal structure characteristic of FSM-16 remained after the 2.89 wt% incorporation of chromium cations. XPS could be used to detect the Cr3+ and Cr6+ species on the surface of Cr-FSM-16. A pre-edge peak that was due to a tetrahedrally coordinated Cr6+ species was confirmed in the XANES spectrum of the Cr-FSM-16, which showed that the coordination state around some Cr species was similar to that around the Si species in FSM-16. With the increase in the amount of chromium cations in FSM-16, its catalytic activity and stability during the oxidative dehydrogenation of isobutane were evidently improved.
|
掲載誌名 |
Journal of the Ceramic Society of Japan
|
ISSN | 13486535
|
出版者 | 公益社団法人 日本セラミックス協会
|
巻 | 123
|
号 | 1444
|
開始ページ | 1084
|
終了ページ | 1089
|
並び順 | 1084
|
発行日 | 2015-12
|
備考 | ©2015 The Ceramic Society of Japan
|
EDB ID | |
出版社版DOI | |
出版社版URL | |
フルテキストファイル | |
言語 |
eng
|
著者版フラグ |
出版社版
|
部局 |
理工学系
|