直近一年間の累計
アクセス数 : ?
ダウンロード数 : ?
ID 109868
著者
エヒロ, タクヤ Department of Chemical Science and Technology, Tokushima University
イタガキ, アイ Department of Chemical Science and Technology, Tokushima University
倉科, 昌 Department of Life System, Institute of Technology and Science, Tokushima University 徳島大学 教育研究者総覧 KAKEN研究者をさがす
加藤, 雅裕 Department of Advanced Materials, Institute of Technology and Science, Tokushima University 徳島大学 教育研究者総覧 KAKEN研究者をさがす
中川, 敬三 Department of Advanced Materials, Institute of Technology and Science, Tokushima University|Department of Resource Circulation Engineering, Center for Frontier Research of Engineering, Tokushima University KAKEN研究者をさがす
カトウ, ユウキ Otake Research Laboratories, Mitsubishi Rayon Co. Ltd.
ニノミヤ, ワタル Otake Research Laboratories, Mitsubishi Rayon Co. Ltd.
杉山, 茂 Department of Advanced Materials, Institute of Technology and Science, Tokushima University|Department of Resource Circulation Engineering, Center for Frontier Research of Engineering, Tokushima University 徳島大学 教育研究者総覧 KAKEN研究者をさがす
キーワード
Template ion exchange
FSM-16
Chromium
Oxidative dehydrogenation
Isobutane
資料タイプ
学術雑誌論文
抄録
The template ion exchange of chromium cations into FSM-16 (#16 Folded Sheets Mesoporous Materials) for 247 h resulted in a 2.89 wt% incorporation of those cations into the FSM-16, although only a 0.3 wt% incorporation had previously been reported. The XRD pattern of the resultant solid (Cr-FSM-16) showed that the hexagonal structure characteristic of FSM-16 remained after the 2.89 wt% incorporation of chromium cations. XPS could be used to detect the Cr3+ and Cr6+ species on the surface of Cr-FSM-16. A pre-edge peak that was due to a tetrahedrally coordinated Cr6+ species was confirmed in the XANES spectrum of the Cr-FSM-16, which showed that the coordination state around some Cr species was similar to that around the Si species in FSM-16. With the increase in the amount of chromium cations in FSM-16, its catalytic activity and stability during the oxidative dehydrogenation of isobutane were evidently improved.
掲載誌名
Journal of the Ceramic Society of Japan
ISSN
13486535
出版者
公益社団法人 日本セラミックス協会
123
1444
開始ページ
1084
終了ページ
1089
並び順
1084
発行日
2015-12
備考
©2015 The Ceramic Society of Japan
EDB ID
出版社版DOI
出版社版URL
フルテキストファイル
言語
eng
著者版フラグ
出版社版
部局
理工学系