Hydrogen Permeability of Palladium Membrane for Steam-Reforming of Bio-Ethanol
Kinouchi, Kouji The University of Tokushima
加藤, 雅裕 The University of Tokushima 徳島大学 教育研究者総覧 KAKEN研究者をさがす
堀河, 俊英 The University of Tokushima 徳島大学 教育研究者総覧 KAKEN研究者をさがす
Yoshikawa, Takushi Sanwa Cornstarch
Wada, Mamoru Sanwa Cornstarch
A Palladium membrane was prepared by electro-less plating method on porous stainless steel. The catalytic hydrogen production by steam-reforming of biomass-derived ethanol (bio-ethanol) using a Pd membrane was analyzed by comparing it with those for the reaction using reagent ethanol (the reference sample). And the hydrogen permeability of the palladium membrane was investigated using the same palladium membrane (H2/He selectivity = 249, at ΔP = 0.10 MPa, 873 K). As a result, for bio-ethanol, deposited carbon had a negative influence on the hydrogen-permeability of the palladium membrane and hydrogen purity. The sulfur content in the bio-ethanol may have promoted carbon deposition. By using a palladium membrane, it was confirmed that H2 yield (%) was increased. It can be attributed that methane was converted from ethanol and produced more hydrogen by steam reforming, due to the in situ removal of hydrogen from the reaction location.
International Journal of Modern Physics: Conference Series
This is an open-access article distributed under the terms of the Creative Commons Attribution 4.0 International License (CCBY)(https://creativecommons.org/licenses/by/4.0/).
ijmpcs_6_7.pdf 257 KB